Short compression testing of multi-ply paperboard, influence from shear strength
Anton Hagman and Mikael Nygårds
Abstract
The influence of the through-thickness shear strength profiles on the short span compression test was examined. This was done both with experiments and finite element simulations on five industrial produced paperboards. It was concluded that the short span compression test is governed by in-plane stiffness and through thickness delamination. The delamination damage was in turn dependent on the local transverse shear strength and in-plane stiffness gradients. Furthermore, it was concluded that the pre-delamination mechanisms were elastic. Finally it was possible to alter the results from the test by altering the shear strength of the paperboard; this should be done uniformly over the entire middle ply of the board if an increased SCT value was what was sought after.
Keywords
Elastic-plastic properties, In-plane compression, Paperboard, Shear
Pages
123-134
DOI
10.3183/NPPRJ-2016-31-01-p123-134
Price
22 EUR (excl. VAT) Buy PDF
Nordic Pulp & Paper Research Journal (NPPRJ) is an international scientific magazine covering science and technology for the areas of wood or bio-mass constituents, pulp and paper and including new fiber-based materials, recovery and by-products from pulping processes, bio-refining and energy issues. Articles meeting required scientific standards are accepted from any continent.
Open Access: Articles not available through Gold Open Access may be purchased by credit card as a pdf file, to be downloaded within 24 h after ordering, at a price of 22 EUR per article. (Value added tax may apply depending on your location, which you enter at payment logout.) Such articles have Green Open Access, i.e. authors may share articles on their personal non-commerical homepage immediately after publication on the website and download them to non-commercial hosting platforms one year after publication in a full issue of NPPRJ.
ISSN: 0283-2631